46-322
IDEAL®* Actual product may vary from image
IDEAL, Heat Shrinkable Tube, Thermo-Shrink, Thin-Wall, Shrink Ratio: 2:1, Outside Diameter: 0.500 IN, Thickness: 026 IN, Length: 6 IN, Dielectric Strength: 20 KV/MM For ASTM D 150 Test Method, Volume Resistivity: 1014 OHM CM For ASTM D 876 Test Method, Continuous Operating Temperature: -55 To 125 DEG C, Minimum Shrink Temperature: 70 DEG C, Heat Shock: No cracking For UL 224(250 DEG C /4 hours), Cable Range: 4 - 1 AWG, Nominal Recoveredi.d. (max.): 0.252 IN, Expanded I.d. (min.): 0.539, Elongation At Break: 600 PCT For ASTM D 638 Test Method, Elongation Of Break After Aging: 350 PCT For UL 224 Test Method, Cold Bend Test (-55°c/4 Hours): No Cracking For UL 224 Test Method, Copper Corrosion: Pass For UL 224 Test Method, Chemical Resistance: Pass For UL 224 Test Method, Longitudinal Shrinkage: 0 Plus Or Minus 5 PCT For UL 224 Test Method, Eccentricity: 30 PCT For UL 224 Test Method, Normal Size: 1/2 IN, Package: Bag
Details
MFG PART #:46-322
McMc Part #:IDEA46322
UPC #:783250463220
Inventory
$195.97 C
**Must be ordered in quantities of 5**
Details
MFG PART #:46-322
McMc Part #:IDEA46322
UPC #:783250463220
Inventory
Attributes
Features
Documentation
Attributes
Brand:IDEAL®
Type:Economy
Voltage Rating:600 VAC
Inner Diameter Expanded:0.539 in
Inner Diameter Recovered:0.252 in
Wall Type:Thin
Wall Thickness Recovered:0.026 in
Wire Size:4 to 1 AWG
Shrink Ratio:2:1
Length:6 in
Temperature Rating:-55 to 125 deg C
Shrink Temperature:70 deg C
Material:Polyolefin
Color:Black
Features
Polyolefin material electrically insulates and protects inline components, disconnect terminals and splices with its high strength and excellent resilience |
Use to bundle wires for very flexible light duty harnesses |
It has highly flame-retardant property to resist electric shock and is flexible for convenient operation |
Resistant to common fluids and solvents |
14 Mpa tensile strength and 20 kV/mil dielectric strength |
It can be elongated up to 350% of the original size after aging at 175 deg C for about 168 hr |
30% eccentricity |
+/-5% longitudinal shrinkage |
-55 deg C/4 hr cold blend test no cracking for UL 224 test method |
Copper corrosion and chemical resistance pass for UL 224 test method |